CMR Materials RE_1-xCa_xMnO₃(RE=La, Nd, A=Ca, Sr) were grown using the floating zone image furnace with halogen lamps as heat source. The growth condition was at 2∼10 mm/hr growth rate in air atmosphere, were 445∼50 rpm and 20∼25 rpm of rotation rate of feedrod and growing crystal, respectively. The grown crystals showed shiny black color and annealed at 1500℃ in a box furnace to release the residual stress during cooling. Characterization analyses of the crystal were carried out using XRD and SEM. The crystal structure of Nd_0.7Ca_0.3MnO₃ was analyzed with smart CCD XRD was lattice parameter of a=5.425(4)Å, b=5.434(4)Å, and c=7.712(5)Å, an orthorombic system with space group of pbnm.