High-temperature superconductor of Bi-2212 system was fabricated by CFP(Centrifugal Forming Process). To make a uniform specimen slurry was prepared in the ratio of 7:3(powder : binder) and ball milled for 24 hours. Milled slurry was charged into a rotating mold with 450 rpm and dried at room temperature. Then the specimen was performed binder burn-out at 35$0^{circ}C$ and heated for partial melting to 86$0^{circ}C$. XRD analysis of most specimens were shown 2212 phase and observed a local plate shped microstructure with a well aligned c-axis direction from SEM images. Measured T$_{c}$(Critical temperature) was about 64 K.K.