The thermal annealing effect of $Zn_{0.9}Cd_{0.1}$ single quantum-well structures grown by molecular beam epitaxy is investigated. As the results of before and after rapid thermal annealed samples a red shift of E1-HH1 peak by Cd interdiffusion during thermal annealing of ZnCeSe/ZnSe sample was observed. In the case of annealed sample over $450^{circ}C$ donor and acceptor impurities related peaks were observed which seems to be due to a diffusion of Ga and As from GaAs substrate. And also interdiffusion phenomena is idenified by the results of DCX measurements and which are consisten with the PL measurements.