In this study the temperature coefficient of resonant frequency(TC $F_{r}$) dielectric and piezoelectric properties of Pb[(S $b_{1}$2//N $b_{1}$2/)$_{0.065}$)-(Z $r_{x}$, $Ti_{1-x}$ )$_{0.90}$] $O_3$ceramics were investigated with Zr/Ti ratio. The compositions near the morphotropic phase boundary (MPB) appeared when Zr/Ti ratio was 49.5/50.5 The dielectric constant and electromechanical coupling factor( $k_{p}$) also showed the highest values of 1,257, 0.653 respectively when the Zr/Ti ratio was 49.5/50.5 Moreover the mechanical quality factor( $Q_{m}$) showed th lowest value of 713 when the Zr/Ti ratio. The temperature coefficient of resonant frequency(TC $F_{r}$) abruptly change at the morphotropic phase boundary(MPB) which existed between the rhombohedral phase with highly negative TC $F_{r}$ of -106ppm/$^{circ}C$ and the tetragonal phase with highly positive TC $F_{r}$ of +64pp $m^{circ}C$ as Zr/Ti ratio varied from 50/50 to 49.5/50.5.50.5..50.5.