The comparative study of texture of Al/Ti thin films deposited on low-dielectric polymer and $SiO_2$substrates has been investigated. Fifty-nm-thick Ti films and 500-nm-thick Al-1%Si-0.5%Cu (wt%) films were deposited sequentially onto low-k polymers and $SiO_2$by using a DC magnetron sputtering system. The texture of Al thin film was determined using X-ray diffraction (XRD) theta-2theta ($ heta$-2$ heta$) and rocking curve and the microstructure of Al/Ti films on low-k polymer and $SiO_2$substrates was characterized by cross-sectional transmission electron microscopy (TEM). Both the $ heta$-2$ heta$ method and rocking curve measurement suggest that Al/Ti thin films deposited on $SiO_2$have stronger texture than those deposited on low-k polymer. The texture of Al thin films strongly depended on that of Ti films. Cross-sectional TEM revealed that grains of Ti films on $SiO_2$substrates had grown perpendicular to the substrate, while the grains of Ti alms on SiLK substrates were formed randomly. The lower degree of (111) texture of Al thin films on low-k polymer was due to Ti underlayer.