The effect of fluid flow on corrosion and erosion-corrosion of metal is a well-recognized phenomenon in pipelines and machinery equipment, and so on. Not only are fluid hydrodynamics important, but also the corrosiveness of the process or production stream affects the corrosion system. Recent research demonstrates that it is possible to erosion-corrosion(E/C) phenomena in terms of hydrodynamics, electrochemical corrosion kinetics and film growth/removal phenomena. Stress corrosion cracking behavior under cavitation erosion-corrosion of mild steel(SS41) was investigated of base metal and weldment under loaded stress. Main result obtained are as follows : 1) The cavitation erosion sensitivity of base metal affected weight loss is more susceptive than heat affected zone, 2) The corrosion sensitivity affected weight loss of welding heat cycle is less susceptive on stress corrosion under cavitation erosion-corrosion than stress corrosion.