Annealing cycle number and nonmagnetic layer thickness dependences of interlayer coupling field ( $H_{inf}$ ) and coercivity ( $H_{cf}$ ) of free magnetic layer on NiMn alloy-spin valve films (SVF) were investigated. The SVF is Glass (7059)/N $i_{81}$F $e_{l9}$(70 $AA$)/Co(10 $AA$)/Cu(t $AA$)/Co(15 $AA$)N $i_{81}$$Fe_{19}$(35 $AA$)/N $i_{25}$M $n_{75}$(250 $AA$)Ta(50 $AA$) films, it were fabricated using the dc sputtering method at different pinning layer thickness and nonmagnetic spacer thickness (Cu thickness; 30 $AA$, 35 $AA$, 40 $AA$) of NiMn alloy with 25 at.%. Ni In case that Cu thickness of SVF is 35 $AA$ and peak exchange coupling field ( $H_{ex}$) was 620 Oe, while coercivity $H_{c}$ = 280 Oe and MR ratio showed 2.5%. As for $H_{inf}$ and $H_{cf}$ , every SVF increased up to the stabilized values with the increase of annealing cycle number 15, which were $H_{inf}$ of 120 Oe and $H_{cf}$ of 75 Oe. The increase of $H_{cf}$ with the annealing cycle number seems to be caused by the effective reduction of Cu layer thickness due to the increase of interfacial mixing of Cu layer and Co layer. In addition, the $H_{inf}$ and $H_{cf}$ dependences of free NiFe layer by the interfacial mixing effect were appeared the different aspects when Cu layer becomes more thinner and thicker than Cu layer thickness of 35 $AA$, respectively.ively....