Highly porous amorphous silica obtained from a serpentine mineral by hydrochloric acid treatment was used to produce a zeolite A through the hydrothermal reaction under atmospheric pressure. An optimum synthesis condition of the zeolite A was achieved at $80^{circ}C$ for two hours with a mole ratio of $Na_2O/SiO_2$1.5. Additionally, it was found that a hydroxysodalite zeolite was formed under the experimental conditions over the reaction temperature of $80^{circ}C$ and the reaction time of 120 minutes even though the crystallization of zeolite proceeds rapidly as the reaction temperature and the alkalinity becomes higher.