Corrosion mechanisms by molten steel and slag were investigated in the zirconia/graphite composite as a material of submerged entry nozzle (SEN) using for producing high quality steel. Most of corrosions were started by the dissolution of zirconia particles into molten steel and oxidation of graphite, but subsequently three modes of corrosion were observed. Firstly, the penetration of slag into zirconia matrix was induced to the diffusion of stabilizing agent outward cubic zirconia grains, and the destabilization of cubic to fine monoclinic zirconia particles, which is enhanced to the decomposition and dissolution of them into slag. Secondly, molten slag penetrates into large cubic zirconia particles along grain boundary and decomposed them to fine cubic grains, which is also enhanced to the dissolution of zirconia grains into slag. Lastly, reaction between carbon and cubic zirconia was formed porous ZrC and enhanced the dissolution of it into slag.