Using the hot-wall epitaxy method, we grew a $Hg_{1-x}Cd_xTe$ (MCT) thin film in-situ after growing (111) CdTe of 9 $mu extrm{m}$ as a buffer layer. The value of FWHM of double crystal x-ray diffraction rocking curve was 125 arcsec and the surface morphology was clean with a small roughness of 10 nm. From measuring the photocurrent of the grown MCT thin film, the maximum peak wavelength and the cut-off wavelength were 1.1050 $mu extrm{m}$ (1.1220 eV) and 1.2632 $mu extrm{m}$ (0.9815 eV), respectively. This peak wavelength corresponds to the peak of the band gap due to the intrinsic transition of the photoconductor. Therefore, the MCT thin film could be used as the photoconducting detector sensing a near-IR wavelength band from 1.0 to 1.6 $mu extrm{m}$.