Poly(ethylene glycol) with number-average molecular weight (M$_{n}$) of 200 (PEG 200) or 400 (PEG 400) was reacted with various linking agents (CH$_2$Cl$_2$, CH$_2$Br$_2$, CH$_2$I$_2$, Br(CH$_2$)$_3$Br) in the presence of alkali to form of oxyalkylene linked chains. Molecular weights of copolymers were controlled using feed mole ratio of alkali/CH$_2$C1$_2$/PEG. The M$_{n}$ of the polymers measured by end group analysis and that measured by GPC agreed well. Molecuglar weights of polyether copolymers obtained from PEG 200 and PEG 400 were about 500~8500 and 1000~2000, respectively. Polyether copolymers prepared from PEG 400 showed melting points of around 1$0^{circ}C$. Glass transition temperatures of the copolymers were around -75$^{circ}C$ and the crystallinity was about 0~25%. The polyether copolymers prepared from PEG 200 had no crystallinity below the M$_{n}$ of 2500. 2500.