A 4㎾ RS840 CO2 laser with a powder auto-feeding apparatus has been used to deposit multiple overlapping tracks of Ni-base superalloy on to low carbon steel. It was found that the surface roughness(turbulence) of an overlapped cladding layer decreased with the increase of the overlapping ratio in an oscillating manner. When the overlapping ratio had values of 0.62, the surface turbulence was lowest. Overlapping ratio offer significant potential for improvement of materials surface properties such as corrosion performance and wear resistance. This paper reports that the overlapping ratio shows best corrosion resistance. The tensile residual stresses generated at the higher overlapping ratio( ＞ 0.45) and the element concentration of Fe increased in the surface layer at the lower overlapping ratio( ＜ 0.45) may lead to worse corrosion resistance.