The object of this study was to investigate the feasibility of solid-phase forming of the composites and to characterize the material behavior in the biaxial stretch forming. The materials tested contained 20%, 30%, and 40% glass fibers by weight in a polypropylene matrix. Biaxial stretch forming tests were performed at three forming speeds of 10mm/sec, 1mm/sec, and 0.1mm/sec and at four forming temperatures of $75^{circ}C, 100^{circ}C, 125^{circ}C, and 150^{circ}C$ to investigate effects of forming speed and forming temperature. The microscopic observation of a formed part was conducted at various strain levels to characterize the material behavior. The strain distribution on a formed part was measured and displayed on the farmed geometry with a contour display The material behavior of the composite in the biaxial stretch forming was strongly influenced by the forming conditions.