In order to investigate the applicability of lyocell fiber to filter paper, papper sheets were manufactured with the addition of lyocell fibers in various length(1.5 denier: 2, 3, 4mm) and content(10, 30, 50%) and their physical characters, such as fibrilation rate, adsorption efficiency of methylene blue(MB), paper formation, and crimping ability, etc, were tested. The level of main fibrilation from lyocell fiber was higher in wet beating process than that in free beating because of the higher strength of lyocell fiber compared with wood fiber. Fibrilation could be observed at the degree of beating over 30$^{circ}$ SR in wet beating with Valley beater. The air permeability and tear factor of the paper increased and the paper formation index decreased according to the increase of fiber length. The weak binding force of lyocell fiber in spite of its higher fiber strength, might be a limitng factor in addition of lyocell fiber to the natural wood pulp in manufacturing the paper having the needed physical properties. High contents of wood pulp decreased air permeability, the breaking length, tear factor, the bursting strength, and paper formation index in paper sheets. As the contents of lyocell increased from 10% to 100%, the adsorption efficiency of MB was elevated to 1.7-7.9 times compared with that in 100% wood pulp. But the length of lyocell fiber did not affect the MB adsorption.