Specimens were cured by using a 1 mm (thickness) ${ imes}$5 mm (diameter) teflon mold, and were immersed in artificial saliva and in 75% ethanol for 1, 7, 14, 21 and 28 days in order to quantify and to identify toxic components and to determine any degra dation byproducts of Bis-GMA that might be released from five commercially available resin-based dental sealants. In artificial saliva, the only released component was triethylene glycol dimethacylate (TEGDMA). In 75% ethanol, TEGDMA, 2,2-bis[4-(2-hydroxy-3-methacryloyloxypropoxy) phenyl]propane (Bis-GMA) and urethane dimethacrylate (UDMA) were released highly at the initial stage, indicating that the amount of component released is not linearly correlated with the immersion time. The amount of released TEGDMA was found to be much higher in 75% ethanol than in artificial saliva. Importantly, bisphenol-A (BPA) was detected from all the uncured sealants tested, suggesting that all the sealants tested contain BPA as a contaminant.