Diamond thin films were synthesized on WC-Co substrate at various experimental parameters using 13.56MHz RF PACVD)radio frequency plasma-assisted chemical vapor deposition). In order to increased the nucleation density, the WC-Co substrate was polished with 3${mu}m$ diamond paste. And the WC-Co substrate was preatreated in $HNO_3;:;H_2O$ = 1:1 and $O_2$ plasma. In $H_2-CH_4$ gas mixture, the crystallinity of thin film increased with decreasing $CH_4$ concentration at 800W discharge power and 20torr reaction pressure. In $H_2-CH_4-O_2$ gas mixture, the crystallinity of thin film increased with increasing $O_2$ concentration at 800W discharge power, 200torr reaction pressure and 4% $CH_4$ concentration.