${eta}$-SiC powder and ${alpha}$-SiC powders of different particle sizes, containing 5.7wt% $Al_2O_3$ and 4.3wt% $Y_2O_3$ as sintering aids, were hot-pressed at $1780^{circ}C$ and subsequently annealed at $1950^{circ}C$ to initiate grain growth. All the hot-pressed and annealed materials consisted of large SiC grains and elongated SiC grains. Typical hardness and fracture toughness of materials for spectacle lens cutting were 15.6 GPa and $5.7MPa{cdot}m^{1/2}$, respectively.