We performed the scientific analysis through composition analysis, micro-structure investigation, melting point and hardness test to the glass beads excavated at Naesanri in Gosung. Through this investigation, we could examine closely the characterization of raw materials and manufacture technique As a result of micro-structure investigation of glass beads, it appeared that the bubbles in glass beads have remained. Coloring agents of yellow glass bead was remained to the shape of inclusion. And on observing the transparent solid particle, we can know that these do not melt the raw materials because of low melting temperature of a crucible. The result of composition analysis of all glass beads using ICP, these were classified as $Na_2O_2$-$SiO_2$ type of glass. Also, these added to $AI_2O_3$ to improve the durability. The value of Vickers hardness of glass beads appeared the HV 490-530. The HV 1,440 of the transparent solid particle was much more than that of inner glass bead. This means that raw materials do not melt because of a low melting temperature of a crucible. The result of melting temperature analysis of glass beads using DSC/TGA, it was measured about $1,250^{circ}C$.