White emission thin film electroluminecent device was fabricated with ZnS for phosphor layers and BST ferroelectric thin film for insulating layers. The ZnS:Mn and $ZnS:SmF_3$ layers were used for emission of red color. Also the $ZnS:TbF_3$ and $ZnS:AgF_3$ layers were used to emission of green and blue color, respectively. And the fabrication conditions of the BST insulating layers were followings, that is, the composition ratio of target, substrate temperature, working pressure and operating gas ratio were $Ba_{0.5}Sr_{0.5}Ti_{0.3}$, $400^{circ}C$, 30 mTorr and 9:1, respectively. The thickness of phosphor were 150 nm for each layers and the insulating layers of upper and bottom were 400 nm and 200 nm, respectively. The luminesence threshold voltage was $75;V_{rms}$ and the maximum brightness of the thin film electroluminecent device was $3200;cd/m^2$ at $100;V_{rms}$.