To obtain representative fatigue crack growth characteristic curve in residual stress field, fatigue crack growth test was carried out at various stress ratio and fatigue crack growth characteristic curve was represented using crack closure concept. Obtained results are as follows;K(sub)op/K(sub)max was independent of K(sub)max when R was lower than 0.5 and crack closure phenomenon was not observed when R is higher than 0.5. therefore neglecting crack closure behaviour, actual fatigue crack growth rate can be underestimated. Thus, considering crack closure phenomenon, fatigue crack growth characteristics curve of A 106 Gr B Steel weldment can be effectively estimated.