The effects of refining load on the paper properties were investigated. HwBKP, SwBKP and SwUKP were refined with PFI mill at the load of 3.33 N/mm and 6.00 N/mm. Higher Scott bond was obtained at the higher refining load for three pulp used in this study. However any changes in the light scattering coefficient with the change of refining load were not observed. Although the effect of refining load on the formation index for SwUKP was not observed, higher refining load gave the better formation for HwBKP and SwBKP. The fiber mass and fiber crowding factor were not affected by the refining load. Higher apparent density and tensile index were obtained with the higher refining load. However, the higher refining load did not improve the tensile index at the same apparent density. The tear index was decreased with the increase of refining load.