The effect of grain shape on the grain growth behavior of oxide system was investigated as afunction of liquid content during liquid phase sintering. As a model system, the solid grains of $Al_{2}O_{3}$ and MgO were selected during liquid phase sintering, i.e. faceted shape of $Al_{2}O_{3}$ in $CaAl_{2}Si_{2}O_{8}$ liquid phase and spherical shape of MgO in $CaMgSiO_{4}$ liquid phase. The average grain size of MgO with spherical shape was decreased with increasing the liquid phase content, whereas that of $Al_{2}O_{3}$ with faceted shape was independent of liquid phase content. In the case of $Al_{2}O_{3}$ grains with faceted shape, which interfaces are expected to be atomically flat, are likely to grow by the interfacial reaction controled process. Whereas, in the case of MgO grains with spherical shape, which interface are expected to be atomically rough, are likely to grow by the diffusion controlled process.