(Ba$_{0.6-x}$Sr$_{0.4}$Ca$_{x}$)TiO$_3$(x=1.10,0.15,0.20) specimens were fabricated by the solid state reaction method and then the structural and dielectric properties as a function of he composition ratio and sintering temperature were studied. As a result of the differential thermal analysis(DTA), exothermic peak was observed at around 102$0^{circ}C$ due to the formation of the polycrystalline perovskite phase. The BSCT(50/40/10) specimen sintered at 150$0^{circ}C$ showed the highest average grain size(18.25${mu}{ extrm}{m}$). The Curie temperature and dielectric constant at room temperature decreased with increasing Ca content. The dielectric constant and dielectric loss of the BSCT(50/40/10) specimen, sintered at 145$0^{circ}C$, were about 4324 and 0.972% at 1KHz, respectively.ively.