Chrome-molybden steel or chrome steel for machine structures has been shown to excellent hardenability adding boron of a small amount at low carbon steel. These days, boron steel has been used high strength bolt and wear resistant components of construction equipment. SEM results showed classical fatigue fractures, consist with surface crack initiation. The specimens were tested repeatedly(9 times) under controlled load rotary bending fatigue tests. In the study, the fatigue crack initiation as well as fatigue crack growth behavior and the fracture mechanism were investigated through observations of fracture of boron steel surface(AISI 51B20).