The effect of sludge digestion on the leaching efficiency of heavy metals from sludge by bioleaching with Thiobacillus thiooxidans MET was investigated. The used sludges were a non- and anaerobically digested. The leaching efficiency of heavy metals was strongly dependent on the pH of the sludge solution rather than the sludge condition and stolid concentration. The lower the pH the more heavy metal was leached from 3.0 of pH. The sequent orders of leaching heavy metals were Zn, Cu, and Cr. Although the buffering capacity of non-digested sludge was similar to anaerobically digested sludge, the pH decrease rate of the anaerobically digested sludge solution was faster than that of the non-digested sludge solution due to the higher sulfur oxidation rate of T. thiooxidans MET in the anaerobically digested sludge. The amount of leached heavy metals from the anaerobically digested sludge showed higher than that of non-digested sludge at the same pH value. This result might be caused by the difference of the insoluble metal types, which were contained in the sludge. An increase in sludge solids concentration decreased the leaching efficiency of heavy metals in the range of solids concentration 10 g/L to 70 g/L. The optimum ratio of S° to sludge stolid was 0.1 in both the sludge. The bioleaching process of heavy metals with T. thiooxidans MET showed the disinfecting effect over 90% as well as the reduction effect in sludge weight of 20%.