Kaiser effects of thermo-acoustic emission (AE) from composite laminates under the repetitive thermal cyclic loads have been quantitatively analyzed in consideration of AE source mechanisms. The repetitive thermal load brought about a large reduction. i.e. an exponential decrease in AE total ringdown counts and AE amplitudes. It was thought that generation of thermo-AE during the first thermal cycle was not caused by crack propagation but by secondary microfracturing due to abrasive contact between crack surfaces. For the repetitive thermal cycles, a few number of weak thermo-AE events were generated due to some frictional sliding contact. Such behavior of thermo-AE showed different characteristics according to specimen kinds and the maximum temperature in the thermal load cycles.