Ginger was stored in the 0.05mm and 0.08mm of PE film bags and the styrofoam box. During the ginger storage, weight losses in the PE film bags were effectively supressed than in the control bag, and storage was better in the 0.08mm PE film bag while the spoilage of ginger was higher than in 0.05mm bag. The effective storage temperature was 10$^{circ}C$ at which was no scouting during the storage. And the perforation in the PE film bag helped the healthy ginger ratio. Single perforation of 6an diameter was good for 0.05mm film and three for 0.08mm film. When CO$_2$absorbent was added into the film bag, the spoilage and mold occurence was lowered. In the styrofoam box, the healthy ginger ratio also increased by incorporating the absorbents, but there were no great differences between activated charcoal and calcium hydroxide.