Conducting perovskite oxide, $(Ba,Sr)RuO_3(BSR)$, which has many advantages for $(Ba,Sr)TiO_3(BST)$ due to their similarity in crystal structure, lattice constant and chemical composition, was prepared on n-type Si (100) by liquid delivery metalorganic chemical vapor deposition(LDMOCVD). The deposition characteristics of BSR were controlled by gas-phase mass-transfer in the experiment. The BSR films deposited at 50$0^{circ}C$ and oxygen flow rate of 100 sccm(standard cc/min) showed an average roughness of 22 $AA$and resistivity of 810 $mu$$Omega$-cm. The roughness of BSR films with oxygen flow rate showed a close relationship with the resistivity of films. BSR (110) peak shifted toward lower Bragg angle with increase of x in the$(Ba_x,Sr_{1-x})TiO_3$. The resistivity of BSR films increased from 810 to 924 $mu$$Omega$-cm with increase of Ba content(x).