The metallurgical study of microconstituents in transient liquid phase bonded joints of Ni-base single crystal superalloys, CMSX-2 and CMSX-4 was investigated employing MBF-80 insert metal. TLP bonding of specimens was carried out at 1,373~1,523K for 0~19.6ks in vacuum. Three types of microconstituents ; needle-like constituent, dot-like constituent and abnormal shape constituent were formed in the bonded interlayer during TLP bonding operation. All these microconstituents were identified as boride. Microconstituents contain a large percentage of Cr in the early stage of bonding. As increasing the holding time, the amount of Cr was decreased and the amount of W, Co and Re were increased. From the analysis results of electron diffraction pattern by TEM, composition of elements in microconstituents were into MBlongrightarrowM$_{5}$B$_3$longrightarrowM$_2$B type with the increased in holding time. It can be explained by the fact that the relative amount of boron in microconstituents was decreased when the holding time was increased.d.