The effect of $V_2O_5$, a donor-type dopant on the degradation of quality factor of ($Zr_{0.8}, Sn_{0.2})TiO_4$was compared with Ta$_2$O$_{5}$ doped ($Zr_{0.8}, Sn_{0.2})TiO_4$ in terms of microstructure, electrical conductivity, and oxidation state of the dopant. It is well known that the addition of the donor type species such as $Ta_2O_5,Nb_2O_5, Sb_2O_5, WO_{3}$, increases the quality factor of ($Zr_{0.8}, Sn_{0.2})TiO_4$due to decrease the oxygen vacancy concentration. Unlike other dopants, however, the addition of $V_2O_5$ decreased the quality factor. The degradation of quality factor of ($Zr_{0.8}, Sn_{0.2})TiO_4$was resulted from the formation of grain boundary phase and $V_2O_5$rich fiber shaped secondary phase, and the increasing the oxygen vacancy concentration due to unstability of oxidation state of vanadium ions in ($Zr_{0.8}, Sn_{0.2})TiO_4$ceramic.c.