Epoxy/$BaTiO_3$composite capacitor films with excellent stability at room temperature, uniform thickness, and electrical properties over a large area ware successfully fabricated. The composite capacitor films with good film formation capability and easy process ability were made from epoxy resin developed for ACF as a matrix and two kinds of $BaTiO_3$powders as fillers to increase the dielectric constant of the composite film. The crystal structure of the powders and its effects on dielectric constant of the films were investigated by X-ray diffraction (XRD). And the optimum amount of dispersant, phosphate ester, was determined by viscosity measurement of suspension. DSC and dielectric property tests were conducted to decide the right curing temperature and the optimum amount of the curing agent. As a result, the capacitors of 7 $mu extrm{m}$ thick film with 10 nF/$ extrm{cm}^2$ and low leakage current were successfully demonstrated.