($Ba_x$$Sr_{1-x}$)$TiO_3$ (x=0.9, 0.7, 0.5) thin films were prepared on ITO-coated glass by sol-gel method. Perovskite phase formation temperature of BST thin films seemed to be higher than $600^{circ}C$. Peaks of perovskite phase shift to high diffraction angles as the Sr/(Ba+Sr) ratio was increased, due to the smaller ionic size of $Sr^{2+}$ than $Ba^{2+}$ . As a heating temperature was increased, the grain became coarser. And as Sr/(Ba + Sr) ratio was increased, the grain became finer. Dielectric constants of the BST(50/50) thin film are higher and dielectric losses of that are lower than those of the others. Dielectric constant and dielectric loss of the BST(50/50) thin film were 652 and 0.042 at 1kHz, respectively.