This study represents the Nondestructive Test about impact damage of composite materials made by different lay-up patterns and degrees. For this study, they were examined by the drop test on composite materials of two type lap-up patterns with fabric and unidirectional prepreg and examined nondestructive test of those. Nondestructive methods were X-ray test with $ZnI_2$ penetrant and Ultrasonic C-scan. The defect detectability of X-ray and Ultrasonic test was compared according to defect species. And the amounts of damage on impacted zone wert compared according to impact energy on two type test specimens. At results, Ultrasonic test was more effective to detect delamination and Penetrant X-ray test was more effective to detect matrix crack and fiber fracture. There were some differences in defect shapes and grades according to lay-up patterns and degrees, and the trend appeared that matrix crack, delamination, fiber fracture occured and increasing defects sizes according to increasing impact energy.