Polymerization of light-activated restorations results in temperature increase caused by both the exothermic reaction process and the energy absorbed during irradiation. Within composite resin, temperature increases up to 2$0^{circ}C$ or more during polymerization. But, insulation of hard tissue of tooth lowers this temperature increase in pulp. However, many clinicians are concerned about intrapulpal temperature injury. The purpose of this study was to evaluate temperature changes in the pulp according to various restorative materials and bases during curing procedure. Caries and restoration-free mandibular molars extracted within three months were prepared Class I cavity of 3$ imes$6mm with high speed handpiece fissure bur. 1mm depth of dentin was evaluated with micrometer in mesial and distal pulp horns. Pulp chambers were filled with 37.0$pm$0.1$^{circ}C$ water to CEJ. Chromium-alumina thermocouple was placed in pulp horn below restorative materials for evaluating of temperature changes. This thermocouple was connected to temperature-recording device(Multiplication analyzer MX, 6.000, JAPAN). Temperature changes was evaluated from initial 37.$0^{circ}C$ after temperature changes to 37.$0^{circ}C$. Tip of curing unit was placed in the center of prepared cavity separated 1mm from restorative materials. Curing time was 40s. The restorative materials were used with Z 100, Fuji II LC, Compoglass flow and bases were used with Vitrebond, Dycal. Resrorative materials were placed in 2mm. The depth of bases were formed in 1mm and in this upper portion, resin of 2mm depth was placed. This procedure was performed 10 times. The results were as follows. 1. All the groups showed that the temperature in pulp increased as curing time increased 2. The temperature increase of glass ionomer was significantly higher than that of Resin and Compomer during curing procedure (P<0.05). 3. The temperature increase in glass ionomer base was significantly higher than that of Calcium hydroxide base during Resin curing procedure (P<0.05).