Surface crack growth characteristics and influence of the stress amplitude in rotary bending fatigue test were evaluated for annealed S35C steel, and than fractal dimensions of fatigue crack paths estimated using the box counting method. The following results that will be helpful to understand the fatigue crack growth mechanism were obtained. (1) Crack growth rate ds/dN and db/dN (s : half crack length at the surface crack, b : crack depth) depended on stress amplitude (${Delta}{sigma}/2$), stress intensity factor range (${Delta}K_A, {Delta}K_C$) and crack length. (2) At the effect area of 0.3 mm hole notch (s＜0.5 mm) crack growth rate did not depend on these factors. (3) The fractal dimensions (D) increased with stress amplitude (${Delta}{sigma}/2$) but decreased with cyclic number.