Green-emitting $Zn_2SiO_4$:Mn phosphor particles having a spherical shape and high luminescence intensities under VUV were prepared by spray pyrolysis process under severe preparation conditions. The type of precursor solutions affected the morphology and luminescence characteristics of the prepared particles. The particles prepared from the clear solution by laboratory-scale process had spherical shape and dense morphology, while the particles prepared from the severe preparation conditions had rough surface and collapsed structure. However, the particles prepared from the colloidal solution utilizing fumed silica were spherical in shape and filled morphology at the severe preparation conditions of high flow rate of carrier gas, high concentration of solution, and large reactor size. The prepared $Zn_2SiO_4$:Mn phosphor particles with complete spherical shape had higher photoluminescence intensity than that of the commercial product prepared by solid state reaction.