Brittle materials such as ceramics and glasses show fragile fracture due to the low toughness and the crack sensitivity. When brittle materials are subjected to impact loading by small spheres, high contact pressure occurs to the surface of the specimen. Local damage is subsequently generated in the specimen. This local damage is a dangerous factor which gives rise to the final fracture of structures. In this research, impact damage of soda-lime glass plates by small spheres was evaluated by considering the effects of impact directions of indenter, pressure condition of specimen and residual strength after impact loading.