In order to investigate the hot cracking phenomena of the Inconel 690 overlay welds, the hot cracking test(modified Varestraint test) was performed by varying augmented strain and welding speed in GTAW. A total of five kinds of specimens was used in the hot cracking test. The specimens used were two kinds of one layer specimens that were composed of just Inconel 690 deposited metal and three kinds of double layer specimens that were composed with as upper part of Inconel 690 weld metal and lower part of SA508 cl.3 or STS 309L. The main results are as fo11ows: In the welds composed of just Inconel 690, as the augmented strain was more increased and the welding speed was more decreased, the extent of cracking was more increased. And these cracks were mainly solidification cracks, and liquation cracks were also observed partially in HAZ. And hot cracking susceptibily of Inconel 690 welds by using filler metals containing Nb were higher than that of the welds with Nb free. The hot cracking susceptibility of Inconel 690 weld metal was increased with dilution of SA 508 cl.3 and STS 309L, and the influence of SA 508 cl.3 was higher than that of 575 309L. The results of calculation of $TSCDelta$ and $TLCDelta$ in Inconel 690 weld metal changed by dilution with base metal or neighboring welds were agreed well with the results of hot cracking test in this study. Therefore, it was expected that the hot cracking was considerably decreased or prevented by using proper welding conditions such as lower heat input, filler metals, base metal and neighboring welds.