Coal fly ash, produced from a power plant in Korea was used for the production of glass-ceramics and the physical properties of glass-ceramics were evaluated. CaO and TiO$_2$ were added into the fly ash during the melting process to reduce the viscosity of molten glass and to induce internal crystallization of glass, respectively. Glass-ceramic was produced through a single stage heat treatment (at 950∼1050$^{C}$ for 37∼240 min) after preparing glass (iota fly ash powder. As a result, a new tiny rod type crystals (a=7.4480, b=10.7381, c=4.3940 A, $alpha$=94.9, $eta$=98.6, γ=108.5°) was found in the glass-ceramics, which showed attractive mechanical properties, high hardness (7.1∼7.6 GPa) and wear resistance (by erosion test). Thus a glass-ceramic produced from thermal power plant fly ash and cell as a source for CaO exhibits a suitable treatment for the recycling and exploitation of waste materials and would be acceptable for a new application far building materials.