The Zr-0.2Sn-0.8Nb-X(X = 0~200ppm Si, 0~0.4wt.% Mo and Mn respectively) ingots for test specimens were manufactured by a vacuum arc re-melting method to find out the effect of Si, Mo, and Mn on the corrosion characteristics of the Zr-0.2Sn-0.8Nb alloy. After being heat-treated and rolled repeatedly out to be flat materials, they were finally heat-treated at 51$0^{circ}C$ for three hours and used as the specimens for corrosion tests. The corrosion behavior of the specimens was studied in both 40$0^{circ}C$ steam for 200 days and in aqueous 70 ppm LiOH solution at 36$0^{circ}C$ for 90 days. From the study it was found that Si from 80 to 200 ppm contributed to increasing the corrosion resistance of Zr-0.2Sn-0.8Nb alloy in both steam and LiOH solution. This study also showed that Mn from 0.1 to 0.4% caused to go up the corrosion resistance, whereas Mo played a apart in improving the corrosion resistance only between 0.05 and 0.2 wt.%.