$SrZrO_3 $resistive oxide barriers on Ag sheathed Bi2223 tapes were prepared by the sol-gel and dip coating method to reduce AC coupling loss. The performance of the dip-coated $SrZrO_3 $ thin films was evaluated in terms of bond strength by varying the Sr/Zr mol ratio and the amount of organic vehicle (ethyl cellulose and a-terpineol) additives. The bond strength of the coatings increased as the Sr/Zr ratio decreased and the amount of organic vehicle rose, respectively. It was found that the effect of organic vehicle addition was more pronounced, suggesting that the adherence of the $SrZrO_3 $ films on Bi2223 tapes was governed primarily by the amount of organic vehicle additive.