We have demonstrated ramp-edge Josephson junctions using high temperature superconductors without depositing artificial barriers. We fabricated a surface barrier formed naturally during an ion beam etching process and the annealing under the oxygen atmosphere. The experimental results imply that the barrier natures such as the resistivity are varied by the annealing conditions and the ion milling conditions including the beam voltages. Thus, the ann eating and etching conditions should be optimized to obtain excellent junction properties. In optimizing the fabricating factors, the interface-controlled junctions showed resistively shunted junctions like current-voltage characteristics and an excellent uniformity. These junctions exhibited a spread ($1sigma$) of $I_{c}$ is 10% fur chips containing 7 junctions at 50K.K.