We have fabricated successfully single-filament composite $MgB_2$/SUS tapes, as an ultrarobust conductor type. The fabrication of the $MgB_2$/SUS tapes was performed by power-in-tube (PIT) process such as swaging and cold rolling. The critical transition temperatures $T_{c}$~38.5 K and ~36 K were observed for the sintered and the nonsintered $MgB_2$/SUS tapes, respectively In addition, the isothermal magnetization M(H) of the sintered $MgB_2$/SUS tapes was measured at temperatures T (between 5 and 50 K) in fields up to 6 T, employing a PPMS-9 (Quantum Design). The persistent current density (J$T_{P}$) values were obtained from the M(H) data, using Bean model, fur the sintered $MgB_2$/SUS tapes. The estimated values were higher than ~ 6$ imes$ $10^{5}$ $A/ extrm{cm}^2$ at T = 5 K, with H : 0 G. We also investigated the cross section of the sintered tapes, by using SEM and EDX. An evidence of weak reaction on boundary between $MgB_2$ and SUS tube is found in the SEM and EDX.X.X.X.