Bis-GMA, 2.2-bis[p(2-hydroxy-3-methacryloyloxypropokyl)phenyl]Propane, is an essential component as a multifunctional methacrylate prepolymer in the light-curable polymeric dental composite resins. Two hydroxyl groups of the Bis-GMA molecule are considered to induce water sorption of the photocured composite resin in a mouth, resulting in gradual long-term deterioration of aesthetics and mechanical properties of the composite resins. In this study, some additives such as light stabilizer and antioxidant were added to composite resins to promote durability and storage stability of the last product. First of all, color change increased as a light stabilizer. Tinuvin P, was added to the composed resins and color stability was improved as an antioxidant, Irganox 245, was added to ones. In addition, when Tinuvin P and Irganox 245 were added together to the composed resins. the color stability was enhanced and mechanical properties such as diametral tensile strength before and after acceleration tests were also not greatly decreased. Therefore, when 0.5 weight Percent of Tinuvin P and 0.1 weight percent of Irganox 245 were added together to dental composite resins. the durability and color stability were enhanced, and furthermore the storage stability was also improved for the composed resins.