NaX zeolite crystals of a uniform particle size of 50 $mu$m were grown by continuous crystallization method from seed crystals (10~20 $mu$m) added into a 0.5~2.0 g mother liquor having a composition $3.5Na_2O : Al_2O_3: 2.1SiO_2: 1000H_2O$. In order to investigate the crystal growing by continuous method, the mother solution was supplied after 7 days, 5 days, 3 days and 1 day, respectively. The seeding resulted in an increase in the fraction of large crystals compared with unseeded batches and successfully led to an uniform NaX zeolite crystal. It was postulated that the seeding in the synthesis mixture leaded out increase of surface area for physical contact reaction and directed growth of seed crystal without the nucleation in the synthesis gel.