A stoichiometric mixture of evaporating materials for CdIn$\_$2/S$\_$4/ single crystal thin films was prepared from horizontal furnace. To obtain the single crystal thin films, CdIn$\_$2/S$\_$4/ mixed crystal was deposited on thoroughly etched semi-insulating GaAs(100) substrate by hot wall epitaxy(HWE) system. The source and substrate temperatures were 630 $^{C}$ and 420 $^{C}$, respectively. The crystalline structure of single crystal thin films was investigated by the photoluminescence and double crystal X-ray diffraction(DCXD). The carrier density and mobility of CdIn$\_$2/S$\_$4/ single crystal thin films measured from Hall effect by van der Pauw method are 9.01$ imes$10$^$16/ cm$^$-3/ and 219 ㎠/V$.$s at 293 K, respectively. From the optical absorption measurement, the temperature dependence of energy band gap on CdIn$\_$2/S$\_$4/ single crystal thin films was found to be Eg(T) ＝ 2.7116 eV - (7.74 $ imes$ 10$^$-4/ eV) T$^$2//(T＋434). After the as-grown CdIn$\_$2/S$\_$4/ single crystal thin films was annealed in Cd-, S-, and In-atmospheres, the origin of point defects of CdIn$\_$2/S$\_$4/ single crystal thin films has been investigated by the photoluminescence(PL) at 10 K. The native defects of V$\_$cd/, V$\_$s/, Cd$\_$int/ and S$\_$int/ obtained by PL measurements were classified as donors or accepters type. And we concluded that the heat-treatment in the S-atmosphere converted CdIn$\_$2/S$\_$4/ single crystal thin films to an optical p-type. Also, we confirmed that In in CdIn$\_$2/S$\_$4/GaAs did not from the native defects because In in CdIn$\_$2/S$\_$4/ single crystal thin films existed in the form of stable bonds.