This study investigated variations of micro-structures and mechanical properties of Ti / STS321L joint with various bonding temperature and time using brazing method. According to increasing bonding temperature and time, it was observed that the thickness of their reaction layer increased due So increasing diffusion rate and time. From the EPMA results, Ti diffused to the STS321L substrate according to increasing bending time to 30min. Hardness of bonded interface increased with increasing bonding temperature and time due to increasing their oxides and intermetallic compounds. XRD data indicated that Ag, Ag-Ti intermetallic compounds, TiAg and $Ti_3Ag$ and titanium oxide, $TiO_2$ were formed in interface. In tensile test, it was found that the tensile strength had a maximum value at the bonding temperature of $900^{circ}C$ and time of 5min, and tensile strength decreased over bonding time of 5min. The critical thickness of intermetallic compounds was observed to about $30mu extrm{m}$, because of brittleness from their excessive intermetallic compounds and titanium oxide, and weakness from void.