Densified cordierite matrixes added alumina platelets were studied as a ceramic substrate material having a low thermal expansion coefficient, low dielectric constant and proper strength. Amorphous-type cordierite powders were filled with four kinds of alumina platelet powders in various compositions. All samples were sintered at $1300^{circ}C$ for 2 h in an air atmosphere. Improved flexural strength of about 80 MPa, low dielectric constant of 5.0 at 1 MHz and low thermal expansion coefficient of $3.5 imes 10^{-6}/^{circ}C$ were obtained by the control of the microstructure. Isolated micropores were formed in the matrix and the porosity was dependent on the platelet content and size. In the 10 vol% of alumina platelet content, the isolated micropores were 3~8 $mu extrm{m}$ in size, and an increase in dielectric constant by adding alumina platelet filler was inhibited by the micropores.