This study was Performed to evaluate the effective solidification of Cd sludge using cement and power plant fly ash as cement admixture, to identify the leaching characteristics of the heavy metal Cd sludge solidified, and to develope proper KLT(Korean Leaching Test) of hazardous waste. KLT was compared with EPT(Extraction Procedure Toxicity) and TCLP(Toxicity Characteristics Leaching Procedure). Fly ash contents ranged from 0% to 30% of cement weight. The experimental results showed that the optimum amount of fly ash replaced was 10% to 15% and KLT was less appropriate than EPA and TCLP. Also the purpose of the study was to suggest the modification factors on the leaching test currently used, based on the above mentioned aspects. The effects of pH, leaching time, leaching for agitating intensity, and leaching solvent were investigated. As the result of test, the leaching potential was relatively high when the pH and agitation intensity of leaching solution were 5 and 150rpm, respectively. Leaching time of six hours was found to be sufficient and the use of acetic acid as a leaching solvent is more useful in landfill site particularly.