This experiment was performed to investigate the characteristics of corrosion mechanism of water steel pipes using SEM(Scanning Electron Microscope) from March 1. 2002 to November 30. The characteristics shown in these results can be summarized as the following: 1. When I investigated to the characteristics of iron pipes and zinc pipes using a SEM, I could be found that there was a distintion in interface between an iron pipe and the scale, and that a zinc pipe wears a dark color. 2. I find much rate of $Fe_2O_3$ and a little rate of FeS as corrosion products, but I hardly find $FeCO_3$without carbon. 3 It was found that the oxide corrosion rate was 0.2~0.3mm/year. And then A-1 was 0.323mm/year that was very high.